Effect of SC Parameters on Material Characteristics for Al 5083-Based Hybrid Matrix Composites Using Taguchi RSM Technique

This research concentrated on material characteristics such as tensile property (TS) and hardness (HV) for AA-5083 manufactured using the stir casting (SC) process. The reinforcing elements silicon carbide (SiC-7.5%) and flyash (FA-5%) in the form of powders will be added to Al alloy to improve the characteristics of composites. Response surface methodology (RSM) was a scientific technique to make optimizing task at stir casting parameters. As per central composite design (CCD), 20 samples (L1-L20) were fabricated at a variation of factors such as stirrer speed (A) 350-550 rpm, stir time (B) 15-35 min, and stir temperature (C) 750-950°C. The result presented that best TS and HV exhibited at experiments L5 (A2-450 rpm, B1-15min, and C1-750°C) and L6 (A1-350 rpm, B1-15min, and C1-750°C). Design expert software (DES) is one of the optimization tools that employed to determine analysis of variance (ANOVA) and the best optimal parameter levels of SC. ANOVA helped to check contribution of SC factors on TS and HV, and it was noticed that mechanical properties were improved with increasing stir speed and stir time but it was reduced with rising of temperature.