Mechanical characteristics evaluation of dual phase and related hardening techniques on AISI 4340 steel

B. M. Gurumurthy, Sathyashankara Sharma, U. Achutha Kini, Ananda Hegde, Ajinkya Patil

Research output: Contribution to journalArticle

Abstract

Steel has wide range of applications and is used in various machinery and general metallic components. Depending on the particular application, steels with tailorable and appropriate properties are used. This requires various methods which can be used to alter the properties based on the requirements. Generally, mechanical properties of the steel are improved by conducting the heat treatment processes. The aim of the present work is to experimentally investigate the effects of conventional heat treatments and special hardening techniques for dual phase structure on mechanical properties of AISI 4340 steel. The test specimens are machined as per ASTM standards and hardness, tensile, impact and microstructure analysis were carried out after the heat treatment processes. Dual phase heat treatment to obtain ferrite-bainite structure is performed by heating the as-bought specimen to the intercritical temperature for two hours followed by isothermal holding in fusible salt bath containing sodium nitrate and sodium nitrite at subcritical temperature for 30 minutes and cooling in air to room temperature. Similarly, ferrite-martensite structure is obtained by air cooling after holding isothermally in the salt bath for 10 seconds. Ferrite-bainite steel was observed to be soft, whereas ferrite-martensite steel was relatively harder. Austempered steel has high toughness with optimum hardness and conventionally hardened steel is the hardest among all. Microstructure shows colony of bainite and martensite in ferrite matrix of ferrite-bainite and ferrite-martensite dual phase structures respectively. An increase in brittleness was observed with the increase in hardness due to the conventional hardening to display lesser impact strength compared to austempered steel.

Original languageEnglish
Pages (from-to)4018-4029
Number of pages12
JournalJournal of Mechanical Engineering and Sciences
Volume12
DOIs
Publication statusPublished - 01-12-2018

Fingerprint

Hardening
Ferrite
Steel
Bainite
Martensite
Heat treatment
Hardness
Phase structure
Sodium
Salts
Cooling
Mechanical properties
Microstructure
Impact strength
Brittleness
Air
Temperature
Toughness
Machinery
Nitrates

All Science Journal Classification (ASJC) codes

  • Computational Mechanics
  • Fuel Technology
  • Energy Engineering and Power Technology
  • Mechanics of Materials
  • Mechanical Engineering
  • Industrial and Manufacturing Engineering

Cite this

@article{57110d69c1d84025a0d1b0b4f4892da0,
title = "Mechanical characteristics evaluation of dual phase and related hardening techniques on AISI 4340 steel",
abstract = "Steel has wide range of applications and is used in various machinery and general metallic components. Depending on the particular application, steels with tailorable and appropriate properties are used. This requires various methods which can be used to alter the properties based on the requirements. Generally, mechanical properties of the steel are improved by conducting the heat treatment processes. The aim of the present work is to experimentally investigate the effects of conventional heat treatments and special hardening techniques for dual phase structure on mechanical properties of AISI 4340 steel. The test specimens are machined as per ASTM standards and hardness, tensile, impact and microstructure analysis were carried out after the heat treatment processes. Dual phase heat treatment to obtain ferrite-bainite structure is performed by heating the as-bought specimen to the intercritical temperature for two hours followed by isothermal holding in fusible salt bath containing sodium nitrate and sodium nitrite at subcritical temperature for 30 minutes and cooling in air to room temperature. Similarly, ferrite-martensite structure is obtained by air cooling after holding isothermally in the salt bath for 10 seconds. Ferrite-bainite steel was observed to be soft, whereas ferrite-martensite steel was relatively harder. Austempered steel has high toughness with optimum hardness and conventionally hardened steel is the hardest among all. Microstructure shows colony of bainite and martensite in ferrite matrix of ferrite-bainite and ferrite-martensite dual phase structures respectively. An increase in brittleness was observed with the increase in hardness due to the conventional hardening to display lesser impact strength compared to austempered steel.",
author = "Gurumurthy, {B. M.} and Sathyashankara Sharma and {Achutha Kini}, U. and Ananda Hegde and Ajinkya Patil",
year = "2018",
month = "12",
day = "1",
doi = "10.15282/jmes.12.4.2018.03.0349",
language = "English",
volume = "12",
pages = "4018--4029",
journal = "Journal of Mechanical Engineering and Sciences",
issn = "2289-4659",
publisher = "Faculty of Mechanical Engineering, Universiti Malaysia Pahang",

}

Mechanical characteristics evaluation of dual phase and related hardening techniques on AISI 4340 steel. / Gurumurthy, B. M.; Sharma, Sathyashankara; Achutha Kini, U.; Hegde, Ananda; Patil, Ajinkya.

In: Journal of Mechanical Engineering and Sciences, Vol. 12, 01.12.2018, p. 4018-4029.

Research output: Contribution to journalArticle

TY - JOUR

T1 - Mechanical characteristics evaluation of dual phase and related hardening techniques on AISI 4340 steel

AU - Gurumurthy, B. M.

AU - Sharma, Sathyashankara

AU - Achutha Kini, U.

AU - Hegde, Ananda

AU - Patil, Ajinkya

PY - 2018/12/1

Y1 - 2018/12/1

N2 - Steel has wide range of applications and is used in various machinery and general metallic components. Depending on the particular application, steels with tailorable and appropriate properties are used. This requires various methods which can be used to alter the properties based on the requirements. Generally, mechanical properties of the steel are improved by conducting the heat treatment processes. The aim of the present work is to experimentally investigate the effects of conventional heat treatments and special hardening techniques for dual phase structure on mechanical properties of AISI 4340 steel. The test specimens are machined as per ASTM standards and hardness, tensile, impact and microstructure analysis were carried out after the heat treatment processes. Dual phase heat treatment to obtain ferrite-bainite structure is performed by heating the as-bought specimen to the intercritical temperature for two hours followed by isothermal holding in fusible salt bath containing sodium nitrate and sodium nitrite at subcritical temperature for 30 minutes and cooling in air to room temperature. Similarly, ferrite-martensite structure is obtained by air cooling after holding isothermally in the salt bath for 10 seconds. Ferrite-bainite steel was observed to be soft, whereas ferrite-martensite steel was relatively harder. Austempered steel has high toughness with optimum hardness and conventionally hardened steel is the hardest among all. Microstructure shows colony of bainite and martensite in ferrite matrix of ferrite-bainite and ferrite-martensite dual phase structures respectively. An increase in brittleness was observed with the increase in hardness due to the conventional hardening to display lesser impact strength compared to austempered steel.

AB - Steel has wide range of applications and is used in various machinery and general metallic components. Depending on the particular application, steels with tailorable and appropriate properties are used. This requires various methods which can be used to alter the properties based on the requirements. Generally, mechanical properties of the steel are improved by conducting the heat treatment processes. The aim of the present work is to experimentally investigate the effects of conventional heat treatments and special hardening techniques for dual phase structure on mechanical properties of AISI 4340 steel. The test specimens are machined as per ASTM standards and hardness, tensile, impact and microstructure analysis were carried out after the heat treatment processes. Dual phase heat treatment to obtain ferrite-bainite structure is performed by heating the as-bought specimen to the intercritical temperature for two hours followed by isothermal holding in fusible salt bath containing sodium nitrate and sodium nitrite at subcritical temperature for 30 minutes and cooling in air to room temperature. Similarly, ferrite-martensite structure is obtained by air cooling after holding isothermally in the salt bath for 10 seconds. Ferrite-bainite steel was observed to be soft, whereas ferrite-martensite steel was relatively harder. Austempered steel has high toughness with optimum hardness and conventionally hardened steel is the hardest among all. Microstructure shows colony of bainite and martensite in ferrite matrix of ferrite-bainite and ferrite-martensite dual phase structures respectively. An increase in brittleness was observed with the increase in hardness due to the conventional hardening to display lesser impact strength compared to austempered steel.

UR - http://www.scopus.com/inward/record.url?scp=85060083150&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85060083150&partnerID=8YFLogxK

U2 - 10.15282/jmes.12.4.2018.03.0349

DO - 10.15282/jmes.12.4.2018.03.0349

M3 - Article

VL - 12

SP - 4018

EP - 4029

JO - Journal of Mechanical Engineering and Sciences

JF - Journal of Mechanical Engineering and Sciences

SN - 2289-4659

ER -